Absorbent cores and methods for forming absorbent cores

ABSTRACT

Pulpless absorbent cores and methods of manufacture are disclosed. A first method for forming an absorbent core may comprise advancing a carrier sheet on a foraminous forming surface in a machine direction, the foraminous forming surface having a width extending in a cross-machine direction, creating a pressure differential across the forming surface, applying a first adhesive onto the carrier sheet, advancing the carrier sheet within a particulate material delivery chamber, and dispensing particulate material from a particulate material inlet within the particulate material delivery chamber to deposit the particulate material onto the first adhesive, wherein the particulate material inlet has a width that is between 25% and 75% of the foraminous forming surface width, and wherein the particulate material is delivered from the particulate material inlet at less than 900 meters per minute.

FIELD OF THE INVENTION

The field of this disclosure relates generally to absorbent cores and methods of manufacturing absorbent cores for use in absorbent articles, and more specifically to pulpless absorbent cores and methods of forming pulpless absorbent cores for use in absorbent articles, such as diapers, training pants, incontinence products, disposable underwear, medical garments, feminine care articles, absorbent swim wear, and the like.

BACKGROUND

Absorbent cores are used in different types of products to control and contain bodily fluids and other bodily liquid discharge. Many present absorbent cores include pulp fluff, or other cellulosic fibers, which act to absorb the discharged liquids. Present absorbent articles can also contain particulate material, for example superabsorbent material, mixed in with the cellulose fibers to greatly increase the absorbent capacity of the absorbent cores. In these instances, the cellulose fibers help to absorb discharged fluids and also to stabilize the superabsorbent material, for instance maintaining the location of the superabsorbent material within the absorbent cores. However, the presence of cellulose fibers in these absorbent cores imparts a significant amount of bulk to the absorbent cores. Accordingly, absorbent cores that have a high absorbent capacity and do not contain cellulose fibers, or do not contain a substantial amount of cellulose fibers, in order to reduce bulk may be desirable.

BRIEF SUMMARY OF THE INVENTION

This disclosure relates generally to absorbent cores and methods of manufacturing absorbent cores for use in absorbent articles, and more specifically to pulpless absorbent cores and methods of forming pulpless absorbent cores for use in absorbent articles, such as diapers, training pants, incontinence products, disposable underwear, medical garments, feminine care articles, absorbent swim wear, and the like.

In a first embodiment, a method of forming an absorbent core may comprise advancing a carrier sheet on a foraminous forming surface in a machine direction, the foraminous forming surface having a width extending in a cross-machine direction, creating a pressure differential across the forming surface, applying a first adhesive onto the carrier sheet, advancing the carrier sheet within a particulate material delivery chamber, and dispensing particulate material from a particulate material inlet within the particulate material delivery chamber to deposit the particulate material onto the first adhesive, wherein the particulate material inlet has a width that is between 25% and 75% of the foraminous forming surface width, and wherein the particulate material is delivered from the particulate material inlet at less than 900 meters per minute.

Additionally, or alternatively, in further embodiments according to the first embodiment, the particulate material may be delivered from the particulate material inlet at less than 600 meters per minute.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the particulate material may be delivered from the particulate material inlet at less than 300 meters per minute.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the particulate material may be delivered to the particulate material inlet in a metered fashion.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the particulate material inlet width may be between 33% and 66% of the foraminous forming surface width.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the foraminous forming surface may have a greatest foraminous forming surface width and a smallest foraminous forming surface width, the smallest foraminous forming surface width being different than the greatest foraminous forming surface width, and wherein the particulate material inlet width may be less than or equal to a smallest foraminous forming surface width.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the carrier sheet may have a left edge region, a central region, and a right edge region, and the particulate material may be deposited onto the first adhesive such that the central region has an average basis weight of particulate material that is at least 110% of an average basis weight of particulate material within at least one of the left edge region and the right edge region.

Additionally, or alternatively, in further embodiments according to the above embodiment, the particulate material may be deposited onto the first adhesive such that the central region has an average basis weight of particulate material that is at least 130% of an average basis weight of particulate material within at least one of the left edge region and the right edge region.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the method may further comprise depositing non-particulate material within the absorbent core region of the forming surface.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the deposited particulate material may comprise superabsorbent material (SAM).

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the particulate material delivery chamber may be a first particulate material delivery chamber, and the method may further comprise applying a second adhesive onto the particulate material deposited onto the first adhesive, advancing the carrier sheet within a subsequent particulate material delivery chamber, and dispensing particulate material from a particulate material inlet within the subsequent particulate material delivery chamber to deposit the particulate material onto the second adhesive, wherein the particulate material inlet within the subsequent particulate material delivery chamber has a width that is between 25% and 75% of the foraminous forming surface width, wherein the particulate material is delivered from the particulate material inlet within the second particulate material delivery chamber at less than 900 meters per minute.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the first adhesive may be a hot-melt adhesive.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the first embodiment, the second adhesive may be a spray-application aqueous binder (SAAB) adhesive.

In a second embodiment, a method for forming an absorbent core may comprise advancing a carrier sheet on a forming member in a machine direction, the forming member having a forming surface defining an absorbent core region, and wherein the absorbent core region has a left edge region and a left edge region width, a central region having a central region width, a right edge region and a right edge region width, and a greatest overall absorbent core region width, applying a vacuum to the forming surface, and depositing a particulate material at a velocity of less than 1200 meters per minute through a particulate material inlet from within a particulate material delivery chamber and onto the carrier sheet within the absorbent core region of the forming surface, wherein the inlet may have an inlet width that is less than the greatest overall absorbent core region width, wherein the central region width may be between 33% and 75% of the greatest overall absorbent core region width, and wherein the particulate material may be deposited onto the carrier sheet within the absorbent core region of the forming surface such that an average basis weight of the particulate material within the central region is at least 110% of an average basis weight of particulate material within at least one of the left edge region and the right edge region.

Additionally, or alternatively, in further embodiments according to the second embodiment, the central region width may be between 62% and 67% of the greatest overall absorbent core region width.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, the absorbent core region further comprises a smallest overall absorbent core region width that is less than the greatest overall absorbent core region width, and the inlet width may be less than the smallest overall absorbent core region width.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, the particulate absorbent may be deposited at a velocity of less than 900 meters per minute through the particulate material inlet and within the absorbent core region of the forming surface.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, the particulate absorbent may be deposited at a velocity of less than 600 meters per minute through the particulate material inlet and within the absorbent core region of the forming surface.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, the particulate absorbent may be deposited at a velocity of less than 300 meters per minute through the particulate material inlet and within the absorbent core region of the forming surface.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, the method may further comprise depositing non-particulate material within the absorbent core region of the forming surface.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, the deposited particulate material may comprise superabsorbent material (SAM).

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, a top portion of the particulate material delivery chamber may be open to allow air to enter the particulate material delivery chamber.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, a top portion of the particulate material delivery chamber is sealed with respect to entry of air.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, the method may further comprise varying the vacuum to adjust an amount of the particulate material that is deposited in the central core portion.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the second embodiment, the method may further comprise depositing a first quantity of the particulate material in a first particulate material delivery chamber and a second quantity of particulate material in a second particulate material delivery chamber.

In a third embodiment, a method for forming an absorbent core may comprise advancing a base carrier sheet in a machine direction on a forming surface, the forming surface having a cross-machine direction width, applying a first adhesive onto a top surface of the base carrier sheet, advancing the base carrier sheet within a first particulate material delivery chamber, depositing a first amount of particulate material onto the first adhesive from a first particulate material inlet disposed within the first particulate material delivery chamber, applying a second adhesive onto the first amount of particulate material outside of the first particulate material delivery chamber, advancing the base carrier sheet with the first adhesive, the first amount of particulate material, and the second adhesive into a second particulate material delivery chamber, depositing a second amount of particulate material onto the second adhesive from a second particulate material inlet disposed within the second particulate material delivery chamber, and applying a top carrier sheet onto the second amount of particulate material, wherein the first particulate material inlet and the second particulate material inlet may have inlet widths that are between 25% and 75% of the cross-machine direction width of the forming surface, and wherein the particulate material may exit the first particulate material inlet and the second particulate material inlet at less than 900 meters per minute.

Additionally, or alternatively, in further embodiments according to the third embodiment, the method may further comprise applying a third adhesive onto the top carrier sheet before applying the top carrier sheet onto the second amount of particulate material.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the third embodiment, the method may further comprise applying a third adhesive onto the second amount of particulate material before applying the top carrier sheet onto the second amount of particulate material, and applying the top carrier sheet onto the third adhesive.

Additionally, or alternatively, in further embodiments according to the above embodiment, the third adhesive may be a spray-application aqueous binder (SAAB) adhesive.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the third embodiment, the first adhesive may be a hot-melt adhesive.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the third embodiment, the second adhesive may be a spray-application aqueous binder (SAAB) adhesive.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the third embodiment, the particulate material may exit the first particulate material inlet and the second particulate material inlet at less than 600 meters per minute.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the third embodiment, the particulate material may exit the first particulate material inlet and the second particulate material inlet at less than 300 meters per minute.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the third embodiment, the method may further comprise depositing non-particulate material onto the base carrier sheet.

In a fourth embodiment, an absorbent core may comprise a layer of adhesive and a layer of particulate material, wherein the absorbent core has a first edge region having a first edge region width, a central region having a central region width, a second edge region having a second edge region width, and an overall core width. The central region width may be between 25% and 75% of the overall core width, and the central region may have an average particulate material basis weight greater than 110% of an average particulate material basis weight of at least one of the first edge region and the second edge region.

Additionally, or alternatively, in further embodiments according to the fourth embodiment, the particulate material may comprise superabsorbent material (SAM).

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fourth embodiment, the particulate material may comprise greater than 90% of a total weight of the absorbent core.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fourth embodiment, the central region width may be between 33% and 66% of the overall core width.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fourth embodiment, the central region may have an average particulate material basis weight greater than 130% of an average particulate material basis weight of at least one of the first edge region and the second edge region.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fourth embodiment, the layer of adhesive may comprise one or more of a hot-melt adhesive and a spray-application aqueous binder (SAAB) adhesive.

In a fifth embodiment, an absorbent core may comprise an elongated outer cover having a central longitudinal axis and an outer cover width, the outer cover further comprising a first edge region having a first edge region width measured perpendicular to the central longitudinal axis, a second edge region having a second edge region width measured perpendicular to the central longitudinal axis, and a central region disposed between the first edge region and the second edge region, the central region having a central region width measured perpendicular to the central longitudinal axis, and particulate material disposed within the elongated outer cover. The central region width may be between 25% and 75% of the outer cover width, and the central region may have an average particulate material basis weight that is at least 110% of an average particulate material basis weight of at least one of the first edge region and the second edge region.

Additionally, or alternatively, in further embodiments according to the fifth embodiment, an average basis weight of particulate material within the absorbent core may decrease along a path from the central longitudinal axis toward an outer edge of the absorbent core.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fifth embodiment, the elongated outer cover may comprise two separate non-woven webs bonded together along their edges.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fifth embodiment, the elongated outer cover may comprise a single non-woven web bonded to itself.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fifth embodiment, the central region may have an average particulate material basis weight that is at least 130% of an average particulate material basis weight of at least one of the first edge region and the second edge region.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fifth embodiment, the central region width may be between 33% and 66% of the outer cover width.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the fifth embodiment, the particulate material may comprise superabsorbent material (SAM).

In a sixth embodiment, an apparatus for forming for forming an absorbent core may comprise a forming drum having a forming surface moveable in a machine direction, wherein the forming surface has a forming surface width extending in a cross-machine direction, a first adhesive applicator configured to apply adhesive at the forming surface, and a first particulate material delivery chamber disposed after the first adhesive applicator in the machine direction, the first absorbent particulate material delivery chamber for dispensing particulate material, the first particulate material delivery chamber including a first particulate material inlet. The apparatus may further comprise a second adhesive applicator disposed after the first particulate material delivery chamber in the machine direction, the second adhesive applicator configured to apply adhesive at the forming surface, and a second particulate material delivery chamber disposed after the second adhesive applicator in the machine direction, the second particulate material delivery chamber for dispensing particulate material, the second particulate material delivery chamber including a second particulate material inlet, wherein each of the first particulate material inlet and the second particulate material inlet may have inlet widths that are between 25% and 75% of the forming surface width.

Additionally, or alternatively, in further embodiments according to the sixth embodiment, the inlet widths may be between 33% and 66% of the forming surface width.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the sixth embodiment, the apparatus may further comprise a third adhesive applicator disposed after the second particulate material delivery chamber in the machine direction, the third adhesive applicator configured to apply adhesive at the forming surface.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the sixth embodiment, the first adhesive applicator may be configured to apply hot-melt adhesive at the forming surface, and wherein the second adhesive applicator may be configured to apply a spray-application aqueous binder (SAAB) adhesive at the forming surface.

Additionally, or alternatively, in further embodiments according to any of the above embodiments with respect to the sixth embodiment, the apparatus may further comprise a fiberizer connected to at least one of the first particulate material delivery chamber and the second particulate material delivery chamber for supplying cellulose fibers to the at least one of the first particulate material delivery chamber and the second particulate material delivery chamber.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic of an example forming assembly for forming absorbent cores.

FIG. 2 is a perspective view of an exemplary forming drum that may be used in the assembly of FIG. 1.

FIG. 3 is a side view of an example forming drum and associated components that may be used in the assembly of FIG. 1.

FIG. 4A is a side view of an exemplary particulate material delivery chamber that may be used in the assembly of FIG. 1.

FIG. 4B is a front view of an exemplary particulate material delivery chamber that may be used in the assembly of FIG. 1.

FIG. 5 is an illustration of an exemplary absorbent core structure that may be produced by the assembly of FIG. 1.

FIG. 6A is a cross-section view of an exemplary absorbent core that may be produced by the assembly of FIG. 1.

FIG. 6B is a cross-section view of an alternative exemplary absorbent core that may be produced by the assembly of FIG. 1.

FIG. 7 is an alternative schematic of an example forming assembly for forming absorbent cores.

FIG. 8 is a cross-section view of an alternative exemplary absorbent core that may be produced by the assembly of FIG. 1 or FIG. 7.

FIG. 9 is a perspective view of a forming drum including a plurality of masking members for forming shaped absorbent cores.

FIG. 10 is a top view of a masking member disposed on the forming drum of FIG. 9.

FIG. 11 is an illustration of an exemplary shaped absorbent core structure that may be produced using the forming drum and masking members of FIGS. 9 and 10.

FIG. 12 is a schematic of an example forming assembly for forming absorbent cores including both cellulose fibers and particulate material.

FIG. 13 depicts a cross-section of an exemplary absorbent core that may for formed by the forming assembly of FIG. 12.

FIGS. 14A and 14B are illustrations of carrier sheets that may be used to form absorbent cores.

FIG. 15 is a front view of an alternate exemplary particulate material delivery chamber that may be used in the assembly of FIG. 1 having a particulate material conduit with an inlet having an inlet width that is smaller than a forming surface width.

FIG. 16 is an illustration of an exemplary absorbent core structure that may be produced by using the particulate material delivery chamber if FIG. 15.

FIG. 17 is an illustration of another exemplary absorbent core structure that may be produced by using the particulate material delivery chamber if FIG. 15.

DETAILED DESCRIPTION OF THE DRAWINGS

When introducing elements of the present invention or the preferred embodiment(s) thereof, the articles “a”, “an”, “the” and “said” are intended to mean that there are one or more of the elements. The terms “comprising”, “including” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements. Moreover, the use of “top”, “bottom”, “above”, “below” and variations of these terms is made for convenience, and does not require any particular orientation of the components.

With reference now to the drawings, FIG. 1 depicts a schematic drawing of an example absorbent core forming apparatus 20, which may be used to form absorbent cores. A few components of apparatus 20 include the forming drum 26 and the particulate material delivery chambers 60 a, 60 b. Accordingly, in some embodiments, apparatus 20 may be used to form absorbent cores comprising particulate material. Superabsorbent material (SAM) is one example of particulate material contemplated by this disclosure. In at least some of these embodiments, the particulate material content of the formed absorbent cores may comprise the majority, by weight, of the contents of the absorbent cores. In other embodiments, the particulate material content of the formed absorbent cores may comprise between 90%-100%, by weight, of the contents of the absorbent cores. These absorbent cores may be described herein as pulpless absorbent cores. As used herein, the phrase pulpless absorbent cores may include both absorbent cores that are truly pulpless and absorbent cores that are only substantially pulpless which have cellulose fibers comprising between 0.5%-10%, by weight, of the total contents of the absorbent cores. Pulpless cores may have one or more advantages relative to absorbent cores that have higher cellulose fiber content. For example, pulpless cores can have absorbent properties, such as absorbent capacity, similar to cores with higher cellulose fiber content. However, pulpless cores can have smaller dimensions than cores having cellulose fiber pulp content. In particular, the pulpless cores may have a reduced thickness in comparison to cores with higher cellulose fiber content.

In the exemplary embodiment of FIG. 1, a base carrier sheet 70 may be unwound from a carrier sheet roll 72. One or more material handling rollers 74 may be used to transport the base carrier sheet 70 proximate forming drum 26. Once in proximity to forming drum 26, the base carrier sheet 70 may be drawn to forming drum 26 by vacuum pressure, described in more detail below in relation to FIGS. 2 and 3. The forming drum 26 rotates in the direction of arrow 10, about drive-shaft 28, advancing the base carrier sheet 70 through one or more absorbent core forming stages, ultimately resulting in the absorbent cores 101. Although absorbent cores 101 are shown as discrete pads, in other embodiments, absorbent cores 101 may be formed as a continuous ribbon.

In some embodiments, the base carrier sheet 70 may comprise a nonwoven material such as a meltblown, spunbond-meltblown-spunbond (SMS), spunlace material, or a natural tissue material. However, in other embodiments, any suitable non-woven material may be used. The base carrier sheet 70 should be at least semi-permeable to air-flow. For instance, the base carrier sheet 70 should be sufficiently permeable such that air is be able to move through the base carrier sheet 70 from a top surface disposed away from the forming surface 24 to a bottom surface disposed proximate the forming surface 24, and ultimately through forming surface 24 into the interior of forming drum 26. Some example suitable dimensions of the base carrier sheet 70 include a width between about 7 cm to about 36 cm. Some example suitable basis weights for the base carrier sheet 70 range from about 5 grams per square meter (gsm) to about 50 gsm. However, the specific dimensions and basis weights used for the base carrier sheet 70 may differ, even outside of these ranges, based on the specific application or desired properties for the absorbent cores 101.

In the example of FIG. 1, the base carrier sheet 70 first moves through first adhesive application zone 80, where adhesive applicator 76 applies adhesive 78 to the base carrier sheet 70. In some examples, the adhesive 78 may be a hot-melt adhesive, such as either a contact hot-melt adhesive or a non-contact hot-melt adhesive. Although, in other examples, adhesive 78 may be any other suitable adhesive for application on a carrier sheet. Further, adhesive 78 may be applied using any suitable application technique or techniques. For instance, adhesive 78 may be applied with a spray application, with a slot-coat application, or by any other appropriate application technique.

After exiting first adhesive application zone 80, the base carrier sheet 70, now containing adhesive 78, is brought in proximity to forming drum 26, where the base carrier sheet 70 is drawn to the forming drum through vacuum pressure. The base carrier sheet then enters particulate material delivery chamber 60 a. Inside of particulate material delivery chamber 60 a, particulate material may be deposited onto the base carrier sheet 70. More specifically, the particulate material may be deposited onto adhesive 78, where the particulate material becomes stabilized, or immobilized on the base carrier sheet 70, by adhesive 78.

The hopper 90 in FIG. 1 may contain particulate material that is delivered to the particulate material delivery chambers 60 a, 60 b. The connecting pipe 68 may connect directly to the hopper 90 in order to transport the particulate material from the hopper 90 to the particulate material delivery chambers 60 a, 60 b. In at least some embodiments, the connecting pipe 68 may include metering device 92. The metering device 92 may be any sort of bulk material metering device, based on volumetric, gravimetric, or mass flow principles, or the like. The metering device 92 may ensure that only a specified amount (for instance, by volume or by weight) of particulate material flows through the connecting pipe per unit of time. Some example suitable ranges for the volume of particulate material flowing through the metering device 92 are between about 5,000 grams per minute (g/min) and about 25,000 g/min. In this manner, the metering device 92 can help to ensure a proper amount of particulate material is delivered to particulate material delivery chambers 60 a, 60 b.

In the example shown in FIG. 1, the connecting pipe 68 may split into delivery pipes 64 and 66. Each of the delivery pipes 64 and 66 may enter the particulate material delivery chambers 60 a, 60 b, forming particulate material delivery conduits 62 a, 62 b. The particulate material delivered to the particulate material delivery chambers 60 a, 60 b may exit the particulate material delivery conduits 62 a, 62 b and be deposited onto the adhesive 78 and the base carrier sheet 70. In some alternative embodiments, instead of a single metering device 92, multiple metering devices may be used to ensure proper delivery of particulate material to each of the particulate material delivery chambers 60 a, 60 b. For example, each of the delivery pipes 64 and 66 may include a metering device, represented by the dashed boxes 93 a and 93 b in FIG. 1, instead the apparatus 20 including metering device 92.

After exiting the particulate material delivery chamber 60 a, the base carrier sheet 70, now containing adhesive 78 and particulate material, may enter second adhesive application zone 81. In some embodiments, second adhesive application zone 81 may be similar to first adhesive application zone 80. For example, in second adhesive application zone 81, adhesive applicator 86 may apply adhesive 88 to the base carrier sheet 70. More specifically, adhesive applicator 86 may apply adhesive 88 onto the particulate material that is stabilized on the base carrier sheet 70. In some embodiments, adhesive 88 may be the same as adhesive 78. For instance, adhesive 88 may also be a hot-melt adhesive, such as a non-contact hot-melt adhesive. Adhesive 88 may also be applied to the base carrier sheet 70 in a similar manner as adhesive 78 was applied to the base carrier sheet 70, such as with a spray application. Although, in other embodiments, adhesive 88 may be a different type of adhesive than adhesive 78 and/or may be applied in a different manner than adhesive 78.

In still other embodiments, adhesive 88 may not be a hot-melt adhesive. In some embodiments, adhesive 88 may be a spray-application aqueous binder (SAAB) adhesive. Where adhesive 88 is a SAAB adhesive, adhesive 88 may be applied with a spray-application. Implementing adhesive 88 as a SAAB adhesive may be preferable in certain embodiments, as SAAB adhesives may be able to better penetrate particulate material than hot-melt adhesives, thereby allowing for greater stabilization of the particulate material deposited onto the base carrier sheet 70.

After passing through second adhesive application zone 81, the base carrier sheet 70 now includes a first adhesive, adhesive 78, disposed on the base carrier sheet 70, a first amount of particulate material 89 (as can be seen in further detail in FIG. 6A) disposed on the adhesive 78, and a second adhesive, adhesive 88, disposed on the first amount of particulate material. The base carrier sheet 70 then enters the particulate material delivery chamber 60 b. In the particulate material delivery chamber 60 b, a second amount of particulate material is deposited onto adhesive 88 in a similar manner as particulate material was deposited onto adhesive 78 in the particulate delivery chamber 60 a.

In some embodiments, the particulate material delivered to the base carrier sheet 70 in the particulate material delivery chambers 60 a, 60 b may be the same type of particulate material. In other embodiments, however, the type of particulate material delivered to the base carrier sheet 70 in the particulate material delivery chamber 60 a may be different than the type of particulate material delivered to the base carrier sheet 70 in the particulate material delivery chamber 60 b. In such embodiments, apparatus 20 may have two separate hoppers that each store different types of particulate material, in contrast to the example of FIG. 1. Additionally, separate connecting and delivery pipes may connect to each of the hoppers and to each of the particulate material delivery chambers 60 a, 60 b to maintain separation of the different particulate material types. Alternatively, apparatus 20 may still include only the single hopper 90 and the connecting and delivery pipes 68, 64, and 66, as shown in FIG. 1. In such embodiments, the hopper 90 may have two separate internal compartments to maintain separation of the different particulate material types. Additionally, connecting pipe 68 may include separate internal lumens. A first of the internal lumens may connect to a first internal compartment of the hopper 90 and to delivery pipe 64, while a second of the internal lumens may connect to a second internal compartment of the hopper 90 and to delivery pipe 66.

As mentioned previously, in some embodiments the particulate material may comprise superabsorbent material (SAM). Suitable superabsorbent materials are well known in the art and are readily available from various suppliers. Example suitable superabsorbent materials may include BASF 9700, available from BASF Corporation, a business having offices located in Charlotte, N.C., U.S.A; and Evonik 5600, available from Evonik Industries, a business having offices located in Parsippany, N.J., U.S.A.

In other embodiments, the particulate material may comprise low- or non-absorbent material such as charcoal, sugar (e.g. xylitol or the like), or encapsulated material. Accordingly, this disclosure contemplates in any of the disclosed embodiments that the delivered particulate material may be either an absorbent material, a non-absorbent material, or both. For instance, absorbent particulate material may be mixed with non-absorbent particulate material, or a first of the particulate material delivery chambers 60 a, 60 b may deliver absorbent particulate material and a second of the particulate material delivery chambers 60 a, 60 b may deliver non-absorbent particulate material.

Once the second amount of particulate material has been deposited onto the base carrier sheet 70, a top carrier sheet 75 may be applied onto the second amount of particulate material. The top carrier sheet 75 may be unwound from a roll 77 of top carrier sheet material, and may be transported proximate the forming drum 26 via one or more material handling rollers 79. After the top carrier sheet 75 has been applied onto the second amount of particulate material, the edges of the top carrier sheet 75 and the base carrier sheet 70 may be bonded together (not shown) to form the pulpless absorbent cores 101. The absorbent cores 101 may then be transported on conveyer 95 for further processing.

In some embodiments, material handling roller 79 may also perform a function similar to a nip roller. For instance, material handling roller 79 may come into close proximity to conveyer 95 in region 99 and the absorbent core 101 may be compressed to reduce bulk and/or to more securely bond the portions of the absorbent core 101 together. In other embodiments, however, one or more separate rollers may perform a nip function, such as rollers 85.

In some alternative embodiments, a third adhesive may be applied to the second amount of particulate material before the top carrier sheet 75 is applied to the second amount of particulate material. In some of these embodiments, apparatus 20 may further include third adhesive application zone 91 a. Where apparatus 20 includes third adhesive application zone 91 a, adhesive applicator 96 a may apply adhesive 98 a to the second amount of particulate material before the top carrier sheet 75 is applied. In various embodiments, adhesive 98 a may be similar to either adhesive 78 or adhesive 88 described previously, and may be applied in any of the previously described methods. In different embodiments, however, apparatus 20 may include third adhesive application zone 91 b instead of third adhesive application zone 91 a. In these embodiments, adhesive applicator 96 b may apply adhesive 98 b directly to the top carrier sheet 75, instead of onto the second amount of particulate material. Additionally, adhesive 98 b may be similar to either adhesive 78 or adhesive 88 described previously, except that adhesive 98 b may not be a SAAB adhesive, as SAAB adhesives may not be suitable for direct application to carrier sheets. Further, adhesive 98 a may be applied in any of the previously described methods. This third adhesive, applied by either adhesive applicator 96 a or adhesive applicator 96 b, may further help to stabilize the second amount of particulate material and/or to more securely attach the top carrier sheet 75 to the second amount of particulate material.

The adhesive applicators 76, 86, and/or 96 a or 96 b may be configured to apply adhesive in a continuous manner in some embodiments. In other embodiments, however, the adhesive applicators 76, 86, and/or 96 a or 96 b may be configured to apply adhesive in an intermittent fashion. For instance, the adhesive applicators 76, 86, and/or 96 a or 96 b may be applied intermittently to target zones on the base carrier sheet 70 to help stabilize the particulate material at locations on the base carrier sheet that will be most effective in absorbing liquid in the resulting absorbent cores due to the placement of the absorbent cores within an absorbent article.

Additionally, in at least some embodiments, the adhesive applicators 76, 86, and/or 96 a or 96 b may apply adhesive in a coordinated, intermittent fashion. In these embodiments, the adhesive applicator 86 may apply adhesive intermittently in a fashion such that the adhesive applicator 86 applies adhesive on top of the adhesive applied by adhesive applicator 76. After application of adhesive by the adhesive applicator 86, the adhesive applied by the adhesive applicator 86 would overlay the adhesive applied by the adhesive applicator 76. In embodiments that include adhesive applicator 96 a or 96 b, the adhesive applicator 96 a or 96 b may apply adhesive in an intermittent fashion such that the adhesive applied by the adhesive applicator 96 a or 96 b overlays the adhesive applied by the adhesive applicator 76 and the adhesive applied by the adhesive applicator 86.

FIGS. 2 and 3 more closely depict portions of apparatus 20, including forming drum 26. The forming drum 26 includes a movable, foraminous forming surface 24, indicated by the hatched pattern in FIG. 2, extending around the circumference of the forming drum 26. The forming drum 26 is mounted on a drive shaft 28 and supported by bearings 30 (as can be seen in FIG. 3). The forming drum 26 includes a circular drum wall (not shown) operatively connected to and rotated by the drum drive shaft 28. The shaft 28 is driven in rotation by a suitable motor or line shaft (not shown) in a clockwise direction as depicted by the arrows in FIG. 3. In some embodiments, the drum wall can be a primary, load-bearing member, and the drum wall can extend generally radially and circumferentially about the drum drive shaft 28.

A vacuum duct 36 located radially inwardly of the forming surface 24 extends over an arc of the interior of the forming drum 26. The vacuum duct 36 is in fluid communication with the forming surface 24 for drawing air through the forming surface 24. The vacuum duct 36 is mounted on and in fluid communication with a vacuum supply conduit 40 connected to a vacuum source 42. The vacuum source 42 may be, for example, an exhaust fan and may create a vacuum within the forming drum which may be between about 2 inches of H₂O to about 40 inches of H₂O. Beyond helping the base carrier sheet 70 adhere to the forming drum 26 as the base carrier sheet 70 advances around the forming drum, the vacuum pressure created by the vacuum source 42 may help to pull the particulate material exiting the particulate material delivery conduits 62 a, 62 b toward the forming surface 24. This vacuum pressure may help to spread the particulate material out on the forming surface 24 and to help form a more even distribution of the particulate material along the cross-machine direction 56 of the base carrier sheet 70.

The vacuum duct 36 is connected to the vacuum supply conduit 40 along an outer peripheral surface of the vacuum supply conduit 40, and extends circumferentially about at least a portion of the vacuum supply conduit 40. The vacuum duct 36 projects radially outwardly from the vacuum supply conduit 40 toward the forming surface 24 and includes axially spaced side walls 34 and angularly spaced end walls 46.

The shaft 28 extends through the drum wall and into the vacuum supply conduit 40 where it is received in the bearing 30. The bearing 30 is sealed with the vacuum supply conduit 40 so that air is not drawn in around the shaft 28 where it enters the vacuum supply conduit 40.

As representatively shown, the vacuum supply conduit 40 can include a conduit end wall 48 and a peripheral wall 50 that delimit the size and shape of the vacuum supply conduit 40. The vacuum supply conduit 40 can have any suitable cross-sectional shape. In the illustrated configuration, the vacuum supply conduit 40 has a generally circular cross-sectional shape. The vacuum supply conduit 40 can be operatively held in position with any suitable support structure. The support structure can also be joined and connected to further components or members that operatively support the portions of the vacuum supply conduit 40 structure that engage the drum drive shaft 28. For example, in the exemplary embodiment, one or more supports may connect to the bearing 30, and the entire vacuum supply conduit 40 may be supported by an overhead mount (not shown).

In the illustrated embodiment, walls 34 extend generally radially and circumferentially about the vacuum supply conduit 40. A drum rim 52 is joined to the walls 34 and is constructed and arranged to provide a substantially free movement of air through the thickness of the drum rim 52. The drum rim 52 is generally cylindrical in shape and extends along the direction of the drum axis 53, and circumferentially about the drum axis 53. As representatively shown, the drum rim 52 can be supported by and extend between the walls 34.

With reference to FIGS. 2 and 3, the forming surface 24 can be provided along the outer, cylindrical surface of the forming drum 26, and can extend along the axial and circumferential dimensions of the forming drum. The circumferential dimension is generally in a machine direction 54 and the axial dimension is generally in a cross-machine direction 56. The structure of the forming surface 24 can be composed of an assembly, and can include a foraminous member 58, which is operatively connected and joined to the forming drum 26. In some contemplated embodiments, the foraminous member 58 may be comprised of a system of multiple inserts. Exemplary foraminous members that may be used in conjunction with the present disclosure are further described in U.S. Pat. No. 6,630,088, titled “Forming media with enhanced air flow properties”, filed on Oct. 23, 2000.

The forming surface 24 can be operatively held and mounted on the drum rim 52 by employing any suitable attachment mechanism. As one representative example, a system of nuts and bolts can be employed to secure the forming surface 24 onto an operative set of mounting rings. In such an example, the mounting rings can be operatively mounted on and secured to the drum rim 52. In other embodiments, the foraminous member 58 may be integral with forming drum 26.

Although not shown in FIG. 2, one or more masking plates may be attached to forming drum 26 on top of forming surface 24, as described in more detail below. The masking plates, for example, may be attached to drum rim 52, or alternately to the foraminous forming member 58. The masking plates may cover a portion of the forming surface 24 in order to block the vacuum in particular portions of the forming surface. The masking plates may allow for differently shaped absorbent cores to be formed on the forming drum 26, as will be explained in more detail below.

Suitable forming drum systems for use with the present disclosure are well known in the art. For example, see U.S. Pat. No. 4,666,647 entitled APPARATUS AND METHOD FOR FORMING A LAID FIBROUS WEB by K. Enloe et al. which issued May 19, 1987; and U.S. Pat. No. 4,761,258 entitled CONTROLLED FORMATION OF LIGHT AND HEAVY FLUFF ZONES by K. Enloe which issued Aug. 2, 1988; the entire disclosures of which are incorporated herein by reference in a manner that is consistent herewith. Other forming drum systems are described in U.S. Pat. No. 6,330,735, entitled APPARATUS AND PROCESS FOR FORMING A LAID FIBROUS WEB WITH ENHANCED BASIS WEIGHT CAPABILITY by J. T. Hahn et al. which issued Dec. 18, 2001, the entire disclosure of which is incorporated herein by reference in a manner that is consistent herewith. Systems for forming surfaces are described in U.S. Pat. No. 6,3630,088, entitled FORMING MEDIA WITH ENHANCED AIR FLOW PROPERTIES by Michael Barth Venturino et al. which issued Oct. 7, 2003, the entire disclosure of which is incorporated herein by reference in a manner that is consistent herewith.

With respect to FIG. 3, additional features of the particulate material delivery chambers 60 a, 60 b are evident. For instance, the particulate material delivery chambers 60 a, 60 b further depict the particulate material delivery conduits 62 a, 62 b terminating in inlets 61 a, 61 b. The inlets 61 a, 61 b, e.g. the plane of the opening of the particulate material delivery conduits 62 a, 62 b, may be positioned within the particulate material delivery chambers 60 a, 60 b such that the inlets 61 a, 61 b are generally parallel with ground 94 and/or with the base of the forming drum 87. In these embodiments, the particulate material delivered from the inlets 61 a, 61 b may exit the inlets 61 a, 61 b in a stream that is substantially perpendicular to the ground 94 and/or the base of the forming drum 87. Additionally, the particulate material delivery chambers 60 a, 60 b are both situated on the top half of the forming drum 26. In this configuration, the particulate material delivered from the particulate material delivery chambers 60 a, 60 b may fall with gravity towards the forming drum, instead of requiring additional energy to push the particulate material to the forming drum 26 against gravity.

However, in other embodiments, the inlets 61 a, 61 b may be tilted with respect to the ground 94 and/or the base of the forming drum 87. For instance, the inlets 61 a, 61 b may form an angle 97 with respect to the ground 94 and/or the base of the forming drum 87 (shown only with respect to inlet 61 a in FIG. 3) having a value of between about 1 degree and about 45 degrees. In even further embodiments, the inlets 61 a, 61 b may form an angle 97 with respect to the ground 94 and/or the base of the forming drum 87 such that the inlets 61 a, 61 b are tangential to the forming drum 26.

FIGS. 4A and 4B depict different close-up views of particulate material delivery chamber 60 a. FIG. 4A depicts a close-up of particulate material delivery chamber 60 a as viewed in the machine direction 54. FIG. 4A further depicts individual particulate material particles 89 exiting inlet 61 a of particulate material delivery conduit 62 a and being deposited onto the base carrier sheet 70. The individual particulate material particles 89 can also be seen disposed and stabilized on the portion of the base carrier sheet 70 after the particulate material delivery chamber 60 a in the machine direction 54.

As mentioned previously, the particulate material may be delivered through particulate material delivery conduit 62 a from the hopper 90, which results in the particulate material being gravity fed to inlet 61 a. In some embodiments, the individual particulate material particles 89 exiting inlet 61 a may exit with a velocity that is less than 1200 meters per minute (m/min). In other embodiments, the individual particulate material particles 89 exiting inlet 61 a may exit with a velocity that is less than 900 m/min. In still other embodiments, the individual particulate material particles 89 exiting inlet 61 a may exit with a velocity that is less than 600 m/min. In yet other embodiments, the individual particulate material particles 89 exiting inlet 61 a may exit with a velocity that is less than 300 m/min. These velocities are in contrast to particulate material that is introduced to a forming chamber pneumatically. Where particulate material is introduced pneumatically, the minimum possible introduction velocity is over 1200 m/min, because that is the velocity at which air needs to move in order to move particulate material particles. Accordingly, gravity feeding the particulate material into the particulate material delivery chamber 60 a allows the individual particulate material particles 89 to be introduced proximate the forming drum 26 with a relatively lower velocity than if the particulate material were to be pneumatically introduced. This lower introduction velocity may allow the individual particulate material particles 89 to be influenced to a greater extent by the vacuum pressure of the forming drum 26. In this manner, the apparatus 20 may be able to achieve a more even distribution of the individual particulate material particles 89 on the base carrier sheet 70 throughout the cross-machine direction 56 than if the individual particulate material particles 89 we introduced into the particulate material delivery chamber 60 a pneumatically.

FIG. 4B depicts an internal view of particulate material delivery chamber 60 a as viewed from the cross-machine direction 56. As can be seen in FIG. 4B, the forming drum 26 may have a drum width 110, and the forming surface 24 may have a forming surface width 111. Generally, the drum width 110 will be greater than the forming surface width 111, as the forming drum 26 will include drum rim 52. However, this is not necessary in all embodiments. FIG. 4B also depicts the forming surface 24 as a relatively uniform and continuous surface. As mentioned previously, an as will be described in more detail below, in different embodiments one or more masking plates may obscure portions of the forming surface 24.

Also shown in FIG. 4B is the particulate material delivery conduit 62 a and inlet 61 a having an inlet width 112. In some embodiments, the inlet width 112 may be the same as the forming surface width 111. However, in other embodiments, the inlet width 112 may be smaller or greater than the forming surface width 111. For instance, the inlet width 112 may be the same as the drum width 110. In other examples, the inlet width 112 may smaller than the forming surface width 111, such as be between about one-quarter and about nine-tenths of the forming surface width 111. Additionally, inlet width 112 may be different for each of particulate material delivery conduits 62 a, 62 b.

The particulate material delivery conduit 62 a may further having a vertical conduit spacing 114 comprising an amount of space between the inlet 61 a of the particulate material delivery conduit 62 a and the forming surface 24. In some examples, the vertical conduit spacing 114 may be between about 15 cm to about 100 cm.

As shown in FIG. 4B, the particulate material delivery chamber 60 a may not be sealed against the forming drum 24. For instance, there may be a gap between the bottom edges 113 of the particulate material delivery chamber 60 a and the forming surface 24 or the forming drum 26. The gap may have a gap space 116 that can be between about 0.5 cm and about 5 cm. In these embodiments, air may be able to enter into the particulate material delivery chamber 60 a through gap space 116, as shown by arrows 117. Entry of air into the particulate material delivery chamber 60 a may push the particulate material 89 toward a center of the forming surface 24 as the particulate material falls from the inlet 61 a to the forming surface 24. This may result in a cross-direction 56 width of the particulate material 89 deposited at the forming surface 24 that is less than inlet width 112. This may result in more particulate material 89 present in a central region of formed absorbent cores than if there were no gap space 116. In some alternative embodiments, gap space 116 may not be disposed between the bottom edges 113 of the particulate material delivery chamber 60 a and the forming surface 26. Rather, the bottom edges 113 of the particulate material delivery chamber 60 a may be sealed against the forming drum 26, and a separate hole may be disposed through a side wall of the particulate material delivery chamber 60 a to allow entry of air into the particulate material delivery chamber 60 a.

Accordingly, in other embodiments, there may not be a gap space 116 between the bottom edges 113 of the particulate material delivery chamber 60 a and the forming surface 24 or the forming drum 26. For instance, the bottom edges 113 of the particulate material delivery chamber 60 a may contact the forming surface 24 or the forming drum 26, or one or more gap fillers (not shown) may be positioned to close up the gap space 116. In these embodiments, there may be no air entering gap space 116. Accordingly, there may be no air impinging on the stream of particulate material 89 and pushing the particulate material 89 inward from the edges of the forming surface 24. In these embodiments, the cross-direction 56 width of the particulate material 89 deposited at the forming surface 24 may be close or equal to the inlet width 112.

In some additional or alternative embodiments, an upper region of the particulate material delivery chamber 60 a may be open and may allow air to flow into the particulate material delivery chamber 60 a as shown by arrows 119. In these embodiments, the inflow of air may cause the particulate material 89 to fall toward the forming surface 24 in a more linear path. For instance, as air enters the particulate material delivery chamber 60 a, the air may be pulled toward the forming surface 24 by the vacuum pressure in the chamber 60 a, and may travel in a generally linear manner. The air may pull the particulate material 89 toward the forming surface 24, and the location of the particulate material 89 deposited at the forming surface 24 may be more heavily influenced by individual starting positions of the particulate material 89 at the inlet 61 a.

However, in still other additional or alternative embodiments, an upper region of the particulate material delivery chamber 60 a may be sealed and may prevent air from entering the particulate material delivery chamber 60 a. In these embodiments, the air within the particulate material delivery chamber 60 a may be more turbulent than in the embodiments where the upper region of the particulate material delivery chamber 60 a allows entry of air, as represented by arrows 121. In these embodiments, the relatively greater turbulence may cause the particulate material 89 to fall in much less linear paths and, therefore, the location of the particulate material 89 deposited at the forming surface 24 may be less dependent on their initial starting position at the inlet 61 a than where the upper region of the particulate material delivery chamber 60 a is open to the air. In at least some of these embodiments, the resulting formed absorbent cores may have a relatively more even distribution of particulate material 89 throughout both the cross-machine direction 56 and the machine direction 54.

Although FIGS. 4A-B only depict particulate material delivery chamber 60 a, it should be understood that particulate material delivery chamber 60 b may be similar to the depicted particulate material delivery chamber 60 a. However, it should also be understood that contemplated embodiments of the present disclosure include apparatuses including particulate material delivery chambers 60 a, 60 b that differ from each other. For instance, particulate material delivery chamber 60 a may include a first set of features that were described above with respect to FIGS. 4A-B, while particulate material delivery chamber 60 b includes a second, different set of features. As one illustrative example, particulate material delivery chamber 60 a may include an inlet, e.g. inlet 61 a, that is oriented generally parallel with respect to ground 94 and/or the base of the forming drum 87 while particulate material delivery chamber 60 b may include an inlet, e.g. inlet 61 b, that is oriented at an angle of 45 degrees with respect to ground 94 and/or the base of the forming drum 87. Of course, this is just one example. More generally, each of the particulate material delivery chambers 60 a, 60 b may include any of the features described above with respect to FIGS. 4A-B, and the specific set of features of each of particulate material delivery chambers 60 a, 60 b may not be the same.

FIG. 5 depicts pulpless absorbent cores 101 as they may appear when exiting apparatus 20. In some examples, the absorbent cores 101 may be formed on a continuous carrier sheet, for instance the base carrier sheet 70 as shown in FIG. 1. As the base carrier sheet 70 including the various adhesives and particulate material exit off of the forming drum 26, another continuous carrier sheet, for instance the top carrier sheet 75, may be applied over the top of the base carrier sheet 70. In this manner, a continuous length of absorbent core may be formed by apparatus 20. However, as mentioned previously, in some embodiments, the forming surface 24 may include one or more masking members which may block a portion of the forming surface 24. In such embodiments, portions of the resulting length of the absorbent core may include gaps where there is no, or relatively little, particulate material content. These gaps are represented by gap regions 115 in FIG. 5. As the absorbent cores 101 were being formed on the forming surface 24, the applied vacuum would have been blocked by the masked portions of the forming surface such that little to no particulate material would have been drawn to the base carrier sheet 70 in gap regions 115. Accordingly, in such embodiments, discrete absorbent cores 101 may be formed on the continuous base carrier sheet 70, as shown in FIG. 5. The base carrier sheet 70 and the top carrier sheet 75 may later be cut, for instance along cut lines 118, in order to form separated absorbent cores. In at least some embodiments, a knife roll may be used to cut the base carrier sheet 70 and the top carrier sheet 75 into separated absorbent cores.

FIG. 6A depicts an example cross-section of an absorbent core 101 taken along line A-A′ in FIG. 5. In the example of FIG. 6A, the absorbent core 101 was formed using only two adhesives. For instance, the absorbent core 101 of FIG. 6A includes the base carrier sheet 70. On top of the base carrier sheet 70 is the first adhesive 120, represented by the ‘x’s. The first adhesive 120, in some embodiments, may comprise and adhesive such as adhesive 78 described with respect to FIG. 1. Adhesive 120 may have been applied to the base carrier sheet 70, for instance, in the first adhesive application zone 80 of FIG. 1.

On top of the first adhesive 120 is the first amount of particulate material 122, represented by particulate material particles 89. The first amount of particulate material 122 may have been applied to the first adhesive 120, for example, in the particulate material delivery chamber 60 a of FIG. 1. The first amount of particulate material 122 may have a thickness of between about 0.1 mm and about 1 mm.

On top of the first amount of particulate material 122 is the second adhesive 124, represented by the ‘w’s. The second adhesive 124, in some embodiments, may comprise an adhesive such as adhesive 88 described with respect to FIG. 1. The second adhesive 122 may have been applied to the first amount of particulate material 122, for instance, in the second adhesive application zone 81 of FIG. 1.

On top of the second adhesive 124 is the second amount of particulate material 126. The second amount of particulate material 126 may have been formed, for example, in the particulate material delivery chamber 60 b of FIG. 1. The second amount of particulate material 126 may have a thickness of between about 0.1 mm and about 1 mm. Finally, the top carrier sheet 75 is shown disposed on top of the second amount of particulate material 126.

In some embodiments, some of the adhesive 124 may penetrate into the first amount of particulate material 122. For instance, in the example of FIG. 6A, strands of the first adhesive 124 (as represented by the ‘w’s) are shown penetrating the first amount particulate material 122 a distance 130. In some examples, distance 130 may range from between about 0.1 mm to about 1 mm. Generally, where the adhesive 124 is a SAAB adhesive, the distance 130 may be on the higher end of the range, as SAAB may be more effective at penetrating the first amount of particulate material 122 than other types of adhesives, such as hot-melt adhesive. The greater penetration distance of SAAB may allow for relatively greater stabilization of the particulate material 89 than other types of adhesive that have lesser penetrating ability.

FIG. 6B depicts an example cross-section of an alternative absorbent core 101′ taken along line A-A′ in FIG. 5. In the example of FIG. 6B, the absorbent core 101′ was formed using three separate adhesive applications. For instance, the absorbent core 101′ of FIG. 6B may be the same as the absorbent core 101 of FIG. 6A except that the absorbent core 101′ of FIG. 6B further includes third adhesive 128, which is also represented by ‘w’s. This is because in the embodiment of FIG. 6B, the second adhesive 124 and the third adhesive 128 are the same adhesive, such as a SAAB adhesive, but may have been applied in separate process steps.

The third adhesive 128, in some embodiments, may comprise adhesive 98 a of FIG. 1. In these examples, the third adhesive 128 may have been applied to the second amount of particulate material 126 in the third adhesive application zone 91 a. As with the second adhesive 120, the third adhesive 128 may penetrate at least partially into the particulate material 89. The penetration distance of the third adhesive 120 is shown by penetration distance 136, which may range from about 0.1 mm to about 2 mm. In at least some embodiments, the third adhesive 128 may penetrate throughout the entire laminate structure of absorbent core 101′.

In other embodiments, however, the third adhesive 128 may not be the same as the second adhesive 124. For instance, in at least some contemplated embodiments, the third adhesive may be applied to the top carrier sheet 75 rather than the second amount of particulate material 126. In these embodiments, the third adhesive may be a hot-melt adhesive rather than a SAAB adhesive, as SAAB adhesives may not be suitable for application to carrier sheets. Accordingly, the third adhesive 128 may be applied to the top carrier sheet such as in third adhesive application zone 91 b of FIG. 1 instead of in third adhesive zone 91 a.

In general, as shown in FIGS. 6A and 6B, absorbent cores 101 and 101′ may have overall thicknesses 123, 125, respectively. Some suitable values for thicknesses 123, 125 range from between about 0.2 mm to about 2.0 mm. However, as will be described in more detail with respect to FIG. 8, the processes described herein may further include additional applications of adhesive and of particulate material, forming even larger laminate structures.

In even further additional or alternative embodiments, one or more tissue or other non-woven sheets may be interspersed between the adhesives and particulate material of the absorbent cores 101, 101′. With specific respect to FIG. 6A, for instance, in some embodiments an intermediate tissue or other non-woven material (not shown) may be placed on top of the first amount of particulate material 122. Then, the second amount of particulate material 126 may be deposited onto that intermediate tissue or other non-woven material. In further embodiments, an adhesive may then be applied to the laminate structure, as shown in FIG. 6B. Although only shown with two separate application of particulate material, as will be described in more detail with respect to FIG. 8, contemplated absorbent cores may include any suitable number of applications of particulate material. Accordingly, in such embodiments, an intermediate tissue or other non-woven sheet may be disposed between each adjacent application of particulate material.

FIG. 7 depicts an alternative pulpless absorbent core forming apparatus 200. Pulpless absorbent core forming apparatus 200 may generally be similar to apparatus 20, except that instead of using a forming drum, pulpless absorbent core forming apparatus 200 uses a planer forming conveyer 226. Although the apparatus 200 may be slightly different from the apparatus 20, the method of forming pulpless absorbent cores with the apparatus 200 is very similar to the process described with respect to apparatus 20. For instance, the base carrier sheet 270 is first fed onto the forming conveyer 226. The base carrier sheet 270 then encounters adhesive application zone 281, where adhesive applicator 276 applies adhesive 278 to the base carrier sheet 270.

Next, the base carrier sheet 270 may enter particulate material delivery chamber 260 a. Particulate material may be delivered to the particulate material delivery chamber 260 a from the hopper 290 through connecting pipe 268 and delivery pipe 264. Delivery pipe 264 may enter the particulate material delivery chamber 260 a and form particulate material delivery conduit 262 a. The particulate material delivered to the particulate material delivery conduit 262 a ultimately exits the particulate material delivery conduit 262 a through inlet 261 a. In some embodiments, a metering device 292 may be present to meter out a specific amount of particulate material from the hopper 290 to ensure a predetermined amount of particulate material flows to particulate material delivery conduit 262 a.

Additionally, in at least some of these embodiments, a vacuum chamber 228 a may be present under the forming conveyer. For instance, the forming conveyer may have a foraminous forming surface (not shown) and air may be able to move across the foraminous forming surface. In the region of vacuum chamber 228 a, air may be moving from within the particulate material delivery chamber 260 a through the foraminous forming surface and into a duct (not shown) coming out of the forming conveyer 226. This movement of air may pull particulate material exiting inlet 261 a toward the forming conveyer to be deposited onto the adhesive 278 and the base carrier sheet 270 forming a layer comprising a first particulate material. Although vacuum ducts 228 a and 228 b are shown only in the vicinity of the particulate material delivery chambers 260 a, 260 b, in other embodiments, vacuum chambers 228 a, 228 b may extend outside of the region around the particulate material delivery chambers 260 a, 260 b and over a greater extent of the forming conveyer 226 than is shown in FIG. 7.

After exiting the particulate material delivery chamber 260 a, the base carrier sheet 270, now including adhesive 278 and a first amount of particulate material, encounters adhesive application zone 281. Within adhesive application zone 281, an adhesive applicator 286 applies adhesive 288 onto the first amount of particulate material that was deposited onto adhesive 278 and the base carrier sheet 270 within the particulate material delivery chamber 260 a.

The base carrier sheet 270 may then enter the particulate material delivery chamber 260 b. Particulate material may be delivered to the particulate material delivery chamber 260 b through connecting pipe 268 and through delivery pipe 266. Delivery pipe 266 may enter the particulate material delivery chamber 260 b and form particulate material delivery conduit 262 b, which in turn may end at inlet 261 b. Particulate material delivered from the hopper 290 may exit inlet 261 b and be drawn toward the adhesive 288 due to vacuum chamber 228 b. Ultimately, a second amount of particulate material may be deposited onto the adhesive 288.

Further processing steps may be included to ultimately form pulpless absorbent cores 301. For instance, in some embodiments, a top carrier sheet (not shown) may be applied over the second amount of particulate material. Additionally, a third adhesive zone 291 may be included where adhesive applicator 296 applies a third adhesive, adhesive 298 onto the second amount of particulate material, or, alternatively, onto the top carrier sheet before the top carrier sheet is applied to the second amount of particulate material. In still further embodiments, the resulting pulpless absorbent cores may be further processed, for example by delivery through a nip roller, or separation by a knife roll. Generally, any of the additional or alternative process steps described with respect to apparatus 20 may also be implemented with respect to apparatus 200.

In further alternative embodiments, it should be understood that the pulpless absorbent cores contemplated by this disclosure are not limited to only two particulate material applications. For instance, FIG. 8 depicts a generic pulpless absorbent core 101″ that may be formed according to the techniques disclosed herein and having any suitable number of particulate material applications. The pulpless absorbent core 101″ includes a base carrier sheet 140, a top carrier sheet 145, and a first amount of particulate material 150 and a second amount of particulate material 151. The pulpless absorbent core 101″ further includes a first adhesive 152 and a second adhesive 153. The adhesives 152, 153 and the first and second amounts of particulate material 150, 151 may be applied in a manner similar to that described with respect to apparatus 20 or 200.

However, pulpless absorbent core 101″ may be formed from any suitable number of additional adhesive and particulate material applications. For instance, each pair of an additional application of adhesive and another amount of particulate material may be thought as a unit building up the absorbent core 101″. Accordingly, apparatus 20 or 200 may be modified to include additional adhesive application zone and particulate material delivery chamber units situated after second adhesive application zone 81 and particulate material delivery chamber 60 b or adhesive application zone 281 and particulate material delivery chamber 260 b. For each additional adhesive application zone and particulate material delivery chamber unit, pulpless absorbent core 101″ may include another adhesive and amount of particulate material. Although the pulpless absorbent core 101″ is contemplated to include any number of suitable additional units of adhesive and particulate material, as indicated by dots 156, some example suitable number of adhesive and particulate material units include 3, 4, 5, 6, and 7.

As mentioned previously, in some embodiments, one or more masking members may be used in order to form shaped pulpless absorbent cores. FIG. 9 depicts forming drum 26 including example masking members 160, although similar masking members may be used with forming conveyer 226. Masking members 160 mask portions of the forming surface 24, creating a pattern of shaped un-masked areas of the forming surface 24. These shaped un-masked areas will affect a distribution of particulate material within the resulting absorbent cores, thereby helping to create the shaped absorbent cores.

Although only shown with one example shape in FIGS. 9 and 10, in other suitable embodiments, the masking members 160 can have any number of different patterns. In still further embodiments, each of the masking members 160 can have different patterns and may be arranged in any order on the forming drum 26. The illustrated system of masking members 160 in FIG. 9 includes substantially identical masking members 160 arranged consecutively around the circumference of the forming drum 26. The masking members 160 can be joined and assembled to the forming drum 26 and/or the forming surface 24 by employing any conventional attaching or mounting mechanisms. For example, the masking members 160 may be secured to the forming surface 24 by a plurality of bolts inserted through holes in the masking members 160 and the forming surface 24.

The masking members 160 may have any shape suitable for mounting onto the forming surface 24. For example, the masking members 160 may have an outer perimeter that forms a substantially rectangular shape. Additionally, the masking members 160 may have a slight curve along their length in the machine direction 54 to form an arc for fitting on the cylindrical forming surface 24. In other suitable embodiments, the masking members 160 may be substantially flat for fitting on planar forming surfaces, such as the planer forming conveyer 226 of apparatus 200. The curve of each masking member 160 may have a radius substantially equal to the radius of the forming surface 24 such that the masking members 160 fit on the forming surface 24. When joined together, a series of masking members 160 can completely concentrically encircle the circumference of the forming surface 24.

FIG. 10 depicts a close-up of one exemplary masking member 160 disposed over the forming surface 24. As can be seen in FIG. 10, masking member 160 includes both masking end portions 162 and masking side portions 164. Masking side portions 164 may extend along the masking member 160 for a distance 166. Some example values of distance 166 may range from about 10 cm to about 30 cm. Additionally, masking side portions 164 may extend inward from the edges of the masking member 160 a distance 168. Some example values of distance 168 may range from about 1 cm to about 5 cm. The masking side portions 164 may act to form a crotch region 170 in the resulting formed absorbent cores.

When the masking members 160 are used within the processes described with respect to apparatus 20 and apparatus 200, the masking members 160 may affect a distribution of particulate material within a resulting absorbent core. As described previously, as the base carrier sheet travels around the forming drum 26, the base carrier sheet may be drawn to the forming surface 24 by the use of a vacuum drawing air through forming surface 24 and into an interior of the forming drum 26. Additionally, as the base carrier sheet travels through a particulate material delivery chamber, the particulate material may be drawn to the base carrier sheet by the vacuum. Where masking members 160 are used, the base carrier sheet travels around the forming drum 26 on top of the masking members 160, which effectively block air moving through the forming surface 24 in the masked areas. Accordingly, as the base carrier sheet travels through a particulate material delivery chamber, the particulate material will be drawn preferentially onto the base carrier sheet over the un-masked areas of the forming surface 24.

FIG. 11 depicts example shaped absorbent cores 201 that may be formed using the masking members 160. In the example of FIG. 11, different regions of the shaped absorbent cores 201 are shown with dashed lines. The shaped absorbent cores 201 may include regions of relatively higher average basis weights, such as within the crotch regions 170 and other regions where the forming surface 24 was un-covered by the masking members 160. The shaped absorbent cores 201 may also include regions of relatively lower average basis weights, such as in end regions 171 and leg regions 173. In embodiments contemplated by this disclosure, the areas of relatively higher average basis weights may have average basis weights ranging from between about 100 grams per meter (gsm) to about 1000 gsm. The areas of relatively lower average basis weights may have average basis weights ranging from between about 0 gsm to about 100 gsm. In some embodiments, the shaped absorbent cores 201 may be separated into individual shaped absorbent cores by cutting the length of resulting shaped absorbent cores 201 in the end regions 171.

The shaped absorbent cores 201 formed using masking members, such as masking members 160, may have some benefits over non-shaped absorbent cores. For instance, the regions of lower basis weights of particulate material may allow the shaped absorbent cores 201 to have a lower overall particulate material content than non-shaped cores, resulting in lower manufacturing costs. However, because of the locations of the areas of higher basis weights, overall absorption performance of the shaped absorbent cores 201 may be at least the same as corresponding non-shaped absorbent cores.

As mentioned previously, the pulpless absorbent cores of the present disclosure may be truly pulpless, or the pulpless absorbent cores may have a relatively small pulp content. For example, some of the pulpless absorbent cores of the present disclosure may include an amount of cellulose fibers that is between about 0.5% and about 10%, by weight, of the total contents of the cores. The addition of a small amount of cellulose fibers to the absorbent cores the present disclosure may impart a greater feeling of softness or provide other beneficial properties to the absorbent cores. FIG. 12 depicts one example apparatus, apparatus 300, which may be used to form the pulpless absorbent cores that have a small pulp content.

Apparatus 300 is very similar to apparatus 20 of FIG. 1. For instance, a base carrier sheet 370 may be fed onto forming drum 326. The base carrier sheet 370 may then advance through a series of adhesive applications zone 380, 381 (and, possibly 391 a or 391 b) and particulate material delivery chambers 360 a, 360 b. A top carrier sheet 375 may then be applied to form the resulting absorbent cores 399.

One difference between apparatus 20 and apparatus 300 is that apparatus 300 may further include fiberizer 340. In the embodiment of FIG. 12, the fiberizer 340 may be fed pulp or cellulose sheets and break up the cellulose sheets into many individual fibers. The fiberizer 340 may be a hammer mill-type fiberizer, or any other suitable type of fiberizer known in the art. The cellulose fibers may exit the fiberizer 340 into delivery ducts 341 and 342. The delivery ducts may ultimately form material delivery chambers 360 a, 360 b.

The material delivery chambers 360 a, 360 b may differ from the particulate material delivery chambers 60 a, 60 b of apparatus 20 in that the material delivery chambers 360 a, 360 b may deliver both particulate material and cellulose fibers to the base carrier sheet. For example, cellulose fibers may travel through the delivery ducts 341, 342 and enter the material delivery chambers 360 a, 360 b. Gravity, along with the vacuum pressure within the material delivery chambers 360 a, 360 b will cause the cellulose fibers to deposit onto the base carrier sheet 370.

Particulate material may also be delivered to the material delivery chambers 360 a, 360 b. For instance, particulate material may be stored in hopper 390 and may be delivered to the material delivery chambers 360 a, 360 b through delivery pipes 364, 366. The delivery pipes 364, 366 may ultimately form particulate material delivery conduits 362 a, 362 b within the material delivery chambers 360 a, 360 b. The delivered particulate material may exit the particulate material delivery conduits 362 a, 362 b within the material delivery chambers 360 a, 360 b. Similar to the pulp fibers, gravity and the vacuum pressure within the material delivery chambers 360 a, 360 b will cause the particulate material to be deposited onto the base carrier sheet 370. In this manner, apparatus 300 may be used to form pulpless absorbent cores containing an amount of cellulose fibers representing between about 0.5% and about 10% of the total weight of the materials within the pulpless absorbent cores.

FIG. 13 depicts a cross-section of an example absorbent core 399 that may be formed by the apparatus 300. FIG. 13 depicts absorbent core 399 including base carrier sheet 370 and top carrier sheet 375. Absorbent core 399 also includes adhesives 378 and 388, represented by ‘x’s and ‘w’s, respectively. In general, the absorbent core 399 may be similar to, and may be formed similarly to, the other absorbent cores of the present disclosure, such as absorbent cores 101, 101′, and 101″. Unlike the previous absorbent cores, however, absorbent core 399 further includes cellulose fibers 393 a, 393 b. As can be seen, cellulose fibers 393, 393 b are disposed intermixed with the individual particulate material particles 389. Cellulose fibers 393 a may be deposited, for instance, along with a first amount of particulate material particles 389, such as in particulate material delivery chamber 360 a of FIG. 12. Cellulose fibers 393 b may be deposited, for instance, along with a second amount of particulate material particles 389, such as in particulate material delivery chamber 360 b of FIG. 12. As mentioned previously the addition of cellulose fibers may impart a greater softness to absorbent cores of the present disclosure, and the cellulose fibers may further help to stabilize the particulate material particles 389 between the base carrier sheet 370 and the top carrier sheet 375.

Again, it should be understood that FIG. 12 only represents one contemplated embodiment. In further embodiments, apparatuses 20 and/or 200 may be modified to include only a single particulate material delivery chamber that further intermixes cellulose fibers with the particulate material before deposition at a forming surface, instead of the two shown with respect to FIG. 12. In general, the apparatuses 20 and/or 200 may include a number of particulate material delivery chambers that allow for the intermixing of cellulose fibers and particulate material that is less than all of the particulate material delivery chambers of the apparatuses. In these alternative embodiments, then, a relatively smaller proportion of the formed absorbent cores may include cellulose fibers. For instance, if the cellulose fibers were intermixed with a first amount of particulate material, the mixture of cellulose fibers and particulate material may be located proximate the base carrier sheet. However, if the cellulose fibers were intermixed with a second (or third, fourth, etc.) amount of particulate material, the mixture of cellulose fibers and particulate material may be located closer to the top carrier sheet than the first amount of particulate material.

In alternative embodiments, instead of forming the pulpless absorbent cores of the present disclosure with both a base carrier sheet and a top carrier sheet, as described previously, some contemplated methods may only use a single carrier sheet. FIGS. 14A and 14B depict example embodiments where a single carrier sheet may be used instead of both a base carrier sheet and a top carrier sheet.

FIG. 14A depicts carrier sheet 405. In some embodiments, carrier sheet 405 may have a first edge region 402 having a first edge 403 and a second edge region 406 having a second edge 407, with a middle region 404 disposed between the first edge region 402 and the second edge region 406. In the embodiment of FIG. 14A, particulate material and adhesive may only be applied within the middle region 404. After application of adhesive and particulate material, instead of applying a second carrier sheet as described herein previously, the second edge region 406 may be folded over the middle region 404 and onto the first edge region 402 such that the second edge 407 is disposed proximate the first edge 403. The edges 403, 407 may then be bonded together to create an enclosed pulpless absorbent core. Bonding the edges 403 and 407 together may be done by any suitable method, such as by pressure bonding, adhesive bonding, ultrasonic bonding, or the like. The apparatuses described herein may be modified to produce such pulpless absorbent cores. For instance, instead of machinery to apply the top carrier sheets, the apparatuses described herein may include folding and bonding machinery, which are well known in the art, to fold the second edge region 406 onto the first edge region 402 and to bond the regions 402, 406 together.

In some embodiments according to FIG. 14A, the carrier sheet 405 may have a width 410. Width 410 may be greater than twice the width of a forming surface used to create pulpless absorbent cores, or alternatively greater than twice the width of an un-masked portion of a forming surface used to create pulpless absorbent cores. In some specific examples, width 410 may range between about 25 cm and about 60 cm.

The middle region 404 may have a width 412. The width 412 may range from between about 40% to about 50% of the overall width 410 of the carrier sheet 405. Additionally, the first edge region 402 may have a width 414 that is be between about 0.5% and about 10% of the overall width 410 of the carrier sheet 405.

FIG. 14B depicts another example embodiment of a single carrier sheet that may be used to form the pulpless absorbent cores of the present disclosure. In the example of FIG. 14B, the carrier sheet 450 may have an overall width 460. The overall width 460 may have values similar to those described with respect to width 410. Additionally, the carrier sheet 450 may have a first edge region 452, a middle region 454, and a second edge region 456. As with the embodiment of FIG. 14A, adhesive and particulate material may only be applied to the carrier sheet 450 within the middle region 454. After application of adhesive and particulate material to the middle region 454, one of the first edge region 452 or the second edge region 456 may be folded over onto the middle region 454. Then, the other of the first edge region 452 or the second edge region 456 may be folded over the middle region 454. In some embodiments, the edge regions 452, 456 may overlap over the middle region 454, and at least a portion of each of the first edge region 452 and the second edge region 456 may be bonded together to form an enclosed pulpless absorbent core.

Similarly to carrier sheet 405, in some embodiments the width 460 of the carrier sheet 450 may be greater than twice the width of a forming surface used to create pulpless absorbent cores, or greater than an un-masked portion of a forming surface used to create pulpless absorbent cores. However, this is not necessary in all embodiments. In at least some embodiments, width 460 may range between about 25 cm and about 60 cm.

The region 454 of the carrier sheet 450 may have a width 462. The width 462 may range from between about 33% to about 50% of the overall width 460 of the carrier sheet 450. In some embodiments, each of the first edge region 452 and the second edge region 456 may have a width (not shown) that is between about 25% and about 33% of the overall width 460. However, the widths of the first edge region 452 and the second edge region 456 do not necessarily need to be equal. For example, the width of the first edge region 452 may be between about 35% and about 40% of the overall width 460 and the width of the second edge region 456 may be between about 10% and about 25% of the overall width of 460, or vice versa.

As mentioned previously with respect to FIG. 4B, the inlet width 112 of particulate material delivery conduits 62 a, 62 b may be less than forming surface width 111 in some embodiments. In some additional or alternative embodiments to any of the embodiments described above, inlet width 112 of particulate material delivery conduits 62 a, 62 b may be less than forming surface width 111 in order to form a pulpless absorbent core having a greater proportion of the particulate material of the absorbent core be deposited within a central region of the absorbent core, as described in more detail below.

FIG. 15 depicts one example embodiment of a particulate material delivery chamber and a forming drum including a particulate material inlet having an inlet width less than the width of the forming surface of the forming drum. Specifically, FIG. 15 depicts a front view of exemplary particulate material delivery chamber 60 a′ and forming drum 26′. As can be seen, the forming drum 26′ may have a drum width 111′, and the forming surface 24′ may have a forming surface width 110′. In such embodiments, the forming surface width 110′ may relate to the width of the unmasked portion of the forming surface 24′, e.g. the width of the absorbent core region 185. Generally, the drum width 111′ will be greater than the forming surface width 110′, as the forming drum 26′ will include drum rim 52′. The exemplary particulate material delivery chamber 60 a′ including particulate material delivery conduit 62 a ′ may be used in the processes described with respect to FIGS. 1 and/or 7. For instance, the specific configuration shown with respect to particulate material delivery chamber 60 a′ may be used for particulate material delivery chamber 60 a (or particulate material delivery chamber 260 a), particulate material delivery chamber 60 b (or particulate material delivery chamber 260 b), or both.

As described previously, in some embodiments, and as shown in FIG. 15, forming drum 26′ may include one or more masking members 183 disposed over the forming surface 24′. Masking member 183 may include masking portions 184a and 184b. The unmasked portion of the forming surface 24′ may represent an absorbent core region 185. The absorbent core region 185 may be split into a central region 186 having a central region width, a left edge region 187 having a left edge region width, and a right edge region 188 having a right edge region width. The widths of the different regions 186, 187, and 188 are described below with respect to FIGS. 16 and 17 depicting example absorbent cores.

Where the masking member 183 includes masking portions such as masking portions 184a, the width of the absorbent core region 185 of the forming surface 24′ may differ depending on where on the forming surface 24′ the width measurement is taken. For instance, in the example of FIG. 15, the forming surface width 110′ may relate to a greatest width of the absorbent core region 185, whereas the forming surface width 180 may relate to the smallest width of the absorbent core region 185.

Also shown in FIG. 15 is the particulate material delivery conduit 62 a ′ and the inlet 61 a′ having an inlet width 112′. As shown, the inlet width 112′ may be generally less than the forming surface width 110′. In some specific contemplated embodiments, the inlet width 112′ may generally be less than the forming surface width 110′, but may be greater than or equal to the forming surface width 180. However, in still other embodiments, the inlet width 112′ may be less than both the forming surface width 110′ and the forming surface width 180. In still more specific embodiments, the inlet width 112′ may have a value that is between about 25% and about 75% of the value of the greatest forming surface width, e.g. forming surface width 110′. In more specific embodiments, the inlet width 112′ may have a value that is between about 33% and about 66% of the value of the forming surface width 110′. In other embodiments, the inlet width 112′ may have a value that is between about 50% and about 150% of the value of the smallest forming surface width, e.g. forming surface width 180. Some example values for the inlet width 112′ range between about 5 cm and about 20 cm.

The particulate material delivery conduit 62 a ′ may further have a vertical conduit spacing 114′ comprising an amount of space between the inlet 61 a′ of the particulate material delivery conduit 62 a ′ and the forming surface 24′. The vertical conduit spacing 114′ may be between about 15 cm and about 100 cm.

Additionally, in some further embodiments, the particulate material delivery chamber 60 a′ may not be sealed against the forming drum 26′. For instance, there may be a gap between the bottom edges 113′ of the particulate material delivery chamber 60 a′ and the forming surface 24′ or the forming drum 26′, represented by gap space 116′. However, in other embodiments, the particulate material delivery chamber 60 a′ may be sealed against the forming drum 26′ to close gap space 116′, or one or more members (not shown) may be disposed about the forming drum 26′, either internally or externally to the particulate material delivery chamber 60 a′, in order to seal gap space 116′. Suitable values for gap space 116′ may be similar to those described previously with respect to FIG. 4B.

Accordingly, in some embodiments, there may be airflow into the particulate material chamber 60 a′ through gap space 116′ between the bottom edges 113′ of the particulate material delivery chamber 60 a′ and the forming surface 24′ or the forming drum 26′, as shown by arrows 117′. Entry of air into the particulate material delivery chamber 60 a′ may push the particulate material 89′ toward a center of the forming surface 24′ as the particulate material falls from the inlet 61 a′ to the forming surface 24′. This may result in a cross-direction 56 width of the particulate material 89′ deposited at the forming surface that is less than the cross-direction 56 width that the particulate material 89′ would have had if there was no airflow through gap space 116′. Or, alternatively, the cross-direction 56 width of the particulate material 89′ deposited at the forming surface 24′ may be the same, but relatively less overall particulate material 89′ may be deposited toward the edges of the forming surface 24′.

However, where there is no gap space 116′, there may be no air impinging on the stream of particulate material 89′ and pushing the particulate material 89′ inward from the edges of the forming surface 24′. In these embodiments, the cross-direction 56 width of the particulate material deposited at the forming surface 24 may be greater than the cross-direction 56 width that the particulate material 89′ would have had if there was airflow through gap space 116′. Or, alternatively, the cross-direction 56 width of the particulate material 89′ deposited at the forming surface 24′ may be the same, but relatively more overall particulate material 89′ may be deposited toward the edges of the forming surface 24′.

In some additional or alternative embodiments, an upper region of the particulate material delivery chamber 60 a′ may be open and may allow air to flow into the particulate material delivery chamber 60 a′ as shown by arrows 119′. In these embodiments, the inflow of air may cause the particulate material 89′ to fall toward the forming surface 24′ in a more linear path. For instance, as air enters the particulate material delivery chamber 60 a′, the air may be pulled toward the forming surface 24′ by the vacuum pressure in the chamber 60 a′, and may travel in a generally linear manner. The air may pull the particulate material 89′ toward the forming surface 24′, and the location of the particulate material 89′ deposited at the forming surface may be more heavily influenced by individual starting positions of the particulate material 89′ at the inlet 61 a′. In these embodiments, the cross-direction 56 width of the particulate material deposited at the forming surface 24 may be lesser than the cross-direction 56 width that the particulate material 89′ would have had if there was no airflow entering through the top of the particulate material delivery chamber 60 a′. Or, alternatively, the cross-direction 56 width of the particulate material 89′ deposited at the forming surface 24′ may be the same, but relatively less overall particulate material 89′ may be deposited toward the edges of the forming surface 24′.

However, in still other additional or alternative embodiments, an upper region of the particulate material delivery chamber 60 a′ may be sealed and may prevent air from entering the particulate material delivery chamber 60 a′. In these embodiments, the air within the particulate material delivery chamber 60 a′ may be more turbulent than in the embodiments where the upper region of the particulate material delivery chamber 60 a′ allows entry of air, as represented by arrows 121′. In these embodiments, the relatively greater turbulence may cause the particulate material 89′ to fall in much less linear paths and, therefore, the location of the particulate material 89′ deposited at the forming surface 24′ may be less dependent on their initial starting position at the inlet 61 a′ than where the upper region of the particulate material delivery chamber 60 a′ is open to the air. This configuration may result in the cross-direction 56 width of the particulate material deposited at the forming surface 24 being greater than the cross-direction 56 width that the particulate material 89′ would have had if there was airflow entering through the top of the particulate material delivery chamber 60 a′. Or, alternatively, the cross-direction 56 width of the particulate material 89′ deposited at the forming surface 24′ may be the same, but relatively more overall particulate material 89′ may be deposited toward the edges of the forming surface 24′.

One of the features of the particulate material delivery chamber 60 a′ disclosed in FIG. 15 is the ability to preferentially distribute the particulate material 89′ exiting the inlet 61 a′ toward a central region of the forming surface 24′. For instance, as described in the embodiment of FIGS. 4A and 4B, the particulate material 89′ may exit the inlet 61 a′ at less than 1200 meters per minute (m/min), less than 900 m/min, less than 600 m/min, or less than 300 m/min. At these speeds, as the vacuum draws the particulate material 89′ toward the forming surface 24′, the vacuum can impact the cross-machine direction 56 spread of the particulate material 89′ as it is deposited at the forming surface 24′. For instance, as can be seen in FIG. 15, particulate material 89′ exiting the inlet 61 a′ may follow different paths towards the forming surface 24′. A portion of the particulate material 89′ may follow a relatively straight path from the inlet 61 a′ toward the forming surface, such as the particulate material 89′ shown directly below the particulate material delivery conduit 62 a ′. However, other portions of the particulate material 89′ may follow paths that extend beyond the inlet 61 a′ in the cross-machine direction 56, such as the particulate material 89′ shown in regions 181 and 182. For these portions of the particulate material 89′, the vacuum diverges the particulate material 89′ exiting the inlet 61 a′ in the cross-machine direction 56.

Accordingly, the particulate material 89′ deposited onto the forming surface 24′ may be preferentially deposited into the central region 186 of the absorbent core region 185. In some contemplated embodiments, the central region 186 of the absorbent core region 185 may have an average basis weight of particulate material 89′ that is greater than 100% of the average basis weight of the particulate material 89′ in the left edge region 187 and/or the right edge region 188. In more specific examples, the central region 186 of the absorbent core region 185 may have an average basis weight of particulate material 89′ that is about 100%, about 110%, about 120%, about 130%, about 140%, or about 150%, or any other suitable percent, of the average basis weight of the particulate material 89′ in the left edge region 187 and/or the right edge region 188.

The specific configuration of the particulate material delivery chamber 60 a′ and the vacuum within the forming drum 26′ may be tuned to produce desired amounts of the particulate material 89′ being deposited in the central region 186 of the absorbent core region 185. For instance, the specific inlet width 112′ and the strength of the vacuum may be chosen to produce the desired amounts of the particulate material 89′ being deposited in the central region 186 of the absorbent core region 185. In general, the vacuum may vary in strength between about 2 inches of H₂O to about 40 inches of H₂O.

In some further additional or alternative embodiments, the strength of the vacuum may be varied to produce different desired amounts of the particulate material 89′ being deposited in the central region 186 of the absorbent core region 185. For instance, the strength of the vacuum may be varied to produce narrower or wider distributions of the particulate material 89′ as desired. Producing narrower or wider distributions may also be achieved by adjusting the inlet width 112′. In even further embodiments, the vacuum may be varied throughout forming of each individual absorbent core to produce varying amounts of the particulate material 89′ deposited onto the central region 186 of the absorbent core region 185 along a machine direction length of an individual absorbent core.

FIG. 16 depicts an example absorbent core 220 that may be formed according to the apparatus disclosed in FIGS. 1, 7, and/or 12 and 15. The absorbent core 220 may have been formed, for example, without masking members, or with masking members that defined a rectangular unmasked portion of the forming surface. Absorbent core 220 may have a similar structure as example absorbent cores 101, 101′, 101″, 201, and/or 399. Absorbent core 220 may have a central longitudinal axis 221 that may correspond to machine direction 54 when absorbent core 220 is being formed on the applicable forming apparatus. The absorbent core 220 may also be divided into three regions: central region 226 having central region width 230, left edge region 227 having left edge region width 231, and right edge region 228 having right region edge width 232. In some embodiments, the central region width 230 may be between about 50% and about 75% of the overall core width 235. Accordingly, the left edge region width 231 and the right edge region width 232 may each comprise between about 12.5% and about 25% of the overall core width 235. In more specific embodiments, the central region width 230 may be between about 62% and about 67% of the overall core width 235. In these embodiments, the left edge region width 231 and the right edge region width 232 may each comprise between about 16.5% and about 19% of the overall core width 235. It should be understood, however, that the left edge region width 231 and the right edge region width 232 do not need to be equal in all contemplated embodiments. Rather, the left edge region width 231 may be either greater or lesser than the right edge region width 232 in different contemplated embodiments. Additionally, these relative width values may be the same for the corresponding regions 186, 187, and 188 of the absorbent core region 185 described with respect to FIG. 15.

Additionally, as absorbent core 220 was formed using the apparatus and methods described with respect to FIG. 15, the regions 226, 227, and 228 may have amounts of particulate material in each region similar to the amounts of particulate material described above with respect to absorbent core region 185 and FIG. 15 being deposited at the forming surface 24′. For instance, in some embodiments, the central region 226 of the absorbent core 220 may have an average basis weight of particulate material that is greater than 100% of the average basis weight of particulate material in the left edge region 227 and/or the right edge region 228. In more specific examples, the central region 226 of the absorbent core 220 may have an average basis weight of particulate material that is about 100%, about 110%, about 120%, about 130%, about 140%, or about 150%, or any other suitable percent, of the average basis weight of the particulate material in the left edge region 227 and/or the right edge region 228. In some even further embodiments, a concentration of particulate material in the absorbent core 220 may generally decrease along a path from the central longitudinal axis 221 toward edges 233 and 234 of the absorbent core 220, or along a path from the boundary of the central region 226 and left edge region 227 or right edge region 228 toward edge 233 or edge 234, respectively.

FIG. 17 depicts another example absorbent core 240 that may be formed according to the apparatus disclosed in FIGS. 1, 7, and/or 12 and 15. In this embodiment, however, the absorbent core 240 may have formed using masking members, such as a masking member 183 depicted in FIG. 15.

Absorbent core 240 may have a similar layered structure as example absorbent cores 101, 101′, 101″, 201, and/or 399. Absorbent core 240 may have a central longitudinal axis 241 that may correspond to machine direction 54 when absorbent core 240 is being formed on the applicable forming apparatus. The absorbent core 240 may also be divided into three regions: central region 246 having a central region width 250, left edge region 247, and right edge region 248. Due to the shaped nature of the absorbent core 240, unlike absorbent core 220, absorbent core 240 may have multiple edge widths. For example, absorbent core 240 may have left edge region widths 251 a, 251 b, and 251 c. Left edge region width 251 a may represent the largest left edge region width while left edge region width 251 c may represent the smallest left edge region width. Likewise, absorbent core 240 may have right edge region widths 252 a, 252 b, and 252c, with right edge region width 252 a representing the largest right edge region width and right edge region width 252 c representing the smallest right edge region width.

In some embodiments, the absorbent core 240 may be truly shaped in that the absorbent core 240 may have the contoured outer shape as shown in FIG. 17. In other embodiments, however, the absorbent core 240 may be shaped but may not have a contoured outer shape. For instance, the absorbent core 240 may still have material disposed within regions 255 and 256 to form a rectangular outer shape. When the absorbent core 240 was being formed, regions 255 and 256 may have been disposed over masking portions of a masking member. Accordingly, in these embodiments, the regions 255 and 256 may have relatively low particulate material content, or no particulate material at all, as the vacuum of the forming drum in the regions 255 and 256 would have been blocked by the masking member. The particulate material exiting the inlet of the particulate material conduit would have been drawn by the vacuum of the forming drum toward the unmasked portions of the forming surface 24′, thereby creating higher concentrations of the particulate material in regions of the absorbent core 240 other than regions 255 and 256.

In some embodiments, the central region width 250 may be between about 50% and about 75% of the overall core width 245. Accordingly, the left edge region width 251 a and the right edge region width 252 a may each comprise between about 12.5% and about 25% of the overall core width 245. In more specific embodiments, the central region width 250 may be between about 62% and about 67% of the overall core width 245. In these embodiments, the left edge region width 251 a and the right edge region width 252 a may each comprise between about 16.5% and about 19% of the overall core width 245. Even further, in some embodiments, the central region 246 may extend across the core 240 such that the values of widths 251 c, 252 c are zero. It should be understood, however, that the left edge region width 251 a and the right edge region width 252 a do not need to be equal in all contemplated embodiments. Rather, the left edge region width 251 a may be either greater or lesser than the right edge region width 252 a in different contemplated embodiments.

In other embodiments, the relative widths of central region 246 and left edge region 247 and right edge region 248 may be measured based on the smallest widths of the left edge region 247 and the right edge region 248. For instance, the left edge region width 251 c and the right edge region width 252 c may each comprise between about 12.5% and about 25% of the overall core width 245. In more specific embodiments, the left edge width region 251 c and the right edge region width 252 c may each comprise between about 16.5% and about 19% of the overall core width 245. Again, it is not necessary that these widths 251 a, 252 a be equal to each other in all embodiments. Also, any of these relative widths may be the same as or similar to the relative widths of the regions 186, 187, and 188 of the absorbent core region 185 described with respect to FIG. 15.

Additionally, as absorbent core 240 was formed using the apparatus and methods described with respect to FIG. 15, the regions 246, 247, and 248 may have amounts of particulate material in each region similar to the particulate material amounts described above with respect to absorbent core region 185 and FIG. 15 being deposited at the forming surface 24′. For instance, in some embodiments, the central region 246 of the absorbent core 240 may have an average basis weight of particulate material that is greater than 100% of the average basis weight of particulate material in the left edge region 247 and/or the right edge region 248. In more specific examples, the central region 246 of the absorbent core 240 may have an average basis weight of particulate material that is about 100%, about 110%, about 120%, about 130%, about 140%, or about 150%, or any other suitable percent, of the average basis weight of the particulate material in the left edge region 247 and/or the right edge region 248. In some even further embodiments, a concentration of particulate material in the absorbent core 240 may generally decrease along a path from the central longitudinal axis 241 toward edges 253 and 254 of the absorbent core 240, or along a path from the boundary of the central region 246 and left edge region 247 or right edge region 248 toward edge 253 or edge 254, respectively.

The pulpless absorbent cores the present disclosure may be used in many different absorbent articles. For example, pulpless absorbent cores the present disclosure may be used in diapers and/or training pants in order to help absorb urine and other liquid discharge from babies and toddlers. The pulpless absorbent cores the present disclosure may additionally, or alternatively, be used in incontinence products, disposable underwear, and/or medical garments to help absorb liquid discharge from people who may not be able to control their ability to urinate or defecate. Even further, the pulpless absorbent cores the present disclosure may additionally, or alternatively, be used in feminine care articles to help absorb vaginal discharges. These are just some example absorbent articles in which the pulpless absorbent cores the present disclosure may be used. In general, the pulpless absorbent cores the present disclosure may be used in any suitable absorbent article application.

As various changes could be made in the above without departing from the scope of the invention, it is intended that all matter contained in the above description and shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense. 

We claim:
 1. A method of forming an absorbent core, the method comprising: advancing a carrier sheet on a foraminous forming surface in a machine direction, the foraminous forming surface having a width extending in a cross-machine direction; creating a pressure differential across the forming surface; applying a first adhesive onto the carrier sheet; advancing the carrier sheet within a particulate material delivery chamber; and dispensing particulate material from a particulate material inlet within the particulate material delivery chamber to deposit the particulate material onto the first adhesive, wherein the particulate material inlet has a width that is between 25% and 75% of the foraminous forming surface width, and wherein the particulate material is delivered from the particulate material inlet at less than 900 meters per minute.
 2. The method of claim 1, wherein the particulate material is delivered from the particulate material inlet at less than 600 meters per minute.
 3. The method of claim 1, wherein the particulate material is delivered from the particulate material inlet at less than 300 meters per minute.
 4. The method of claim 1, wherein the particulate material is delivered to the particulate material inlet in a metered fashion.
 5. The method of claim 1, wherein the particulate material inlet width is between 33% and 66% of the foraminous forming surface width.
 6. The method of claim 1, wherein the foraminous forming surface has a greatest foraminous forming surface width and a smallest foraminous forming surface width, the smallest foraminous forming surface width being different than the greatest foraminous forming surface width, and wherein the particulate material inlet width is less than or equal to a smallest foraminous forming surface width.
 7. The method of claim 1, wherein the carrier sheet has a left edge region, a central region, and a right edge region, and wherein the particulate material is deposited onto the first adhesive such that the central region has an average basis weight of particulate material that is at least 110% of an average basis weight of particulate material within at least one of the left edge region and the right edge region.
 8. The method of claim 1, wherein the particulate material delivery chamber is a first particulate material delivery chamber, and further comprising: applying a second adhesive onto the particulate material deposited onto the first adhesive; advancing the carrier sheet within a subsequent particulate material delivery chamber; and dispensing particulate material from a particulate material inlet within the subsequent particulate material delivery chamber to deposit the particulate material onto the second adhesive, wherein the particulate material inlet within the subsequent particulate material delivery chamber has a width that is between 25% and 75% of the foraminous forming surface width, and wherein the particulate material is delivered from the particulate material inlet within the second particulate material delivery chamber at less than 900 meters per minute.
 9. A method for forming an absorbent core comprising: advancing a carrier sheet on a forming member in a machine direction, the forming member having a forming surface defining an absorbent core region, and wherein the absorbent core region has a left edge region and a left edge region width, a central region having a central region width, a right edge region and a right edge region width, and a greatest overall absorbent core region width; applying a vacuum to the forming surface; and depositing a particulate material at a velocity of less than 1200 meters per minute through a particulate material inlet from within a particulate material delivery chamber and onto the carrier sheet within the absorbent core region of the forming surface, wherein the inlet has an inlet width that is less than the greatest overall absorbent core region width, wherein the central region width is between 33% and 75% of the greatest overall absorbent core region width, and wherein the particulate material is deposited onto the carrier sheet within the absorbent core region of the forming surface such that an average basis weight of the particulate material within the central region is at least 110% of an average basis weight of particulate material within at least one of the left edge region and the right edge region.
 10. The method of claim 9, wherein the central region width is between 62% and 67% of the greatest overall absorbent core region width.
 11. The method of claim 9, further comprising depositing non-particulate material within the absorbent core region of the forming surface.
 12. The method of claim 9, wherein the deposited particulate material comprises superabsorbent material (SAM).
 13. The method of claim 9, wherein the absorbent core region further comprises a smallest overall absorbent core region width that is less than the greatest overall absorbent core region width, and wherein the inlet width is less than the smallest overall absorbent core region width.
 14. The method of claim 9, wherein a top portion of the particulate material delivery chamber is open to allow air to enter the particulate material delivery chamber.
 15. The method of claim 9, wherein a top portion of the particulate material delivery chamber is sealed with respect to entry of air.
 16. A method for forming an absorbent core, the method comprising: advancing a base carrier sheet in a machine direction on a forming surface, the forming surface having a cross-machine direction width; applying a first adhesive onto a top surface of the base carrier sheet; advancing the base carrier sheet within a first particulate material delivery chamber; depositing a first amount of particulate material onto the first adhesive from a first particulate material inlet disposed within the first particulate material delivery chamber; applying a second adhesive onto the first amount of particulate material outside of the first particulate material delivery chamber; advancing the base carrier sheet with the first adhesive, the first amount of particulate material, and the second adhesive into a second particulate material delivery chamber; depositing a second amount of particulate material onto the second adhesive from a second particulate material inlet disposed within the second particulate material delivery chamber; and applying a top carrier sheet onto the second amount of particulate material, wherein the first particulate material inlet and the second particulate material inlet have inlet widths that are between 25% and 75% of the cross-machine direction width of the forming surface, and wherein the particulate material exits the first particulate material inlet and the second particulate material inlet at less than 900 meters per minute.
 17. The method of claim 16, further comprising applying a third adhesive onto the top carrier sheet before applying the top carrier sheet onto the second amount of particulate material.
 18. The method of claim 16, further comprising: applying a third adhesive onto the second amount of particulate material before applying the top carrier sheet onto the second amount of particulate material; and applying the top carrier sheet onto the third adhesive.
 19. The method of claim 18, wherein the third adhesive is a spray-application aqueous binder (SAAB) adhesive.
 20. The method of claim 16, wherein the second adhesive is SAAB adhesive. 